Loctite 542 Equvialent Hydraulic Thread Sealant for Fine Threads

          Loctite 542 Equvialent  Hydraulic Thread Sealant for Fine Threads

                                                                              from Tina(hengying@cnhybond.com 0086-18927302778 Skype:hengying11)

1:PRODUCT DESCRIPTION

Hybond542 provides the following product characteristics:

Technology: Acrylic

Chemical Type: Dimethacrylate ester

Appearance (uncured): Brown liquidLMS

MSComponents: One component - requires no mixing

Viscosity: low

Cure : Anaerobic

Secondary Cure: Activator

Application :Thread sealing

Strength: Medium 

CNHYBOND 542 is designed for the locking and sealing of metal pipes and fitting. the product cures when confined in the absence of air between close fitting metal surfaces and prevents loosening and leakage from shock and vibration, the thixotropic nature of cnhybond 542 reduces the migration of liquid product after application to the substrate. 

2: TYPICAL PROPERTIES OF UNCURED MATERIAL

Specific Gravity @ 25 °C 1.08

Flash Point - See MSDS

Viscosity, Brookfield - RVT, 25 °C, mPa·s (cP):

Spindle 2, speed 2.5 rpm 1200 to 2755LMS

3:TYPICAL PERFORMANCE OF CURED MATERIAL

Adhesive Properties

After 24 hours @ 22 °C

Breakaway Torque, ISO 10964:

M10 steel nuts and bolts N·m 15

(lb.in.) (130)

Prevail Torque, ISO 10964:

M10 steel nuts and bolts N·m 9

(lb.in.) (80)

Breakloose Torque, ISO 10964, Pre-torqued to 5 N·m:

M10 steel nuts and bolts N·m 24

(lb.in.) (220)

Max. Prevail Torque, ISO 10964, Pre-torqued to 5 N·m:

M10 steel nuts and bolts N·m 426

(lb.in.) (220)

Compressive Shear Strength, ISO 10123:

Steel pins and collars N/mm² ≥6LMS

(psi) (≥900

4:For Assembly

For Porosity Sealing

(1). For best results ,clean all surfaces(external and internal)with a cnhyond cleaning solvent and allow to dry

(2). If the material is an inactive metal or the cure speed is to slow spray all threads with activator 712 and allow to dry

(3). Apply a 360 degree bead of product to the leading threads of the male fitting ,leaving the first thread free. Force the material into the threads to thouroughly fill the voids.for bigger threads and voids, adjust product amount accourdingly and apply a 360degree bead of product on the female threads also

(4). Using accepted trade practices, assemble and wrench tighten fittings until proper alignment is obtained.

(5). Properly tightened fittings will seal instantly to moderate pressures , For maximum pressure resistance and solvent resistance allow the product to cure a minimum of 24 hours

5:For Disassembly

(1). Remove with standard hand tools.

(2). In rare instances where hand tools do not work because of excessive engagement length, apply localized heat to nut or bolt to approximately 250 °C. Disassemble while HOT

6:For Clean up

Cured product can be removed with a combination of soaking in a HENG YING solvent and mechanical abrasion such as a wire brush.

7:Storage

Store product in the unopened container in a dry location. Storage information may be indicated on the product container labeling.

Optimal Storage: 8 °C to 21 °C. Storage below 8 °C or greater than 28 °C can adversely affect product properties. Material removed from containers may be contaminated during use. Do not return product to the original container.CNHYBOND Corporation cannot assume responsibility for product which

has been contaminated or stored under conditions other than those previously indicated. If additional information is required, please contact us.

Loctite 648 Equivalent High Strength High Temperature Fast Cure Retaining Compound

Loctite 648 Equivalent High Strength High Temperature Fast Cure Retaining Compound          from Tina(hengying@cnhybond.com   0086-18927302778  Skype:hengying11)

1:Product Description 

HYBOND 648 provides the following product characteristics:

Technology: Acrylic

Chemical Type: Urethane methacrylate

Appearance (uncured): Green liquidLMS

MComponents:  One component - requires no mixing

Viscosity: Low

Cure : Anaerobic

Secondary Cure: Activator

Application: Retaining

Strength: high

HYBOND 648™ is designed for the bonding of cylindrical fitting parts. The product cures when confined in the absence of air between close fitting metal surfaces and prevents loosening and leakage from shock and vibration. Typical applications include holding gears and sprockets onto gearbox shafts and rotors on electric motor shafts

2: Typical Properties of uncured material 

Specific Gravity @ 25 °C 1.13

Flash Point - See MSDS:

Viscosity, Brookfield - RVT, 25 °C, mPa·s (cP):

Spindle 2, speed 20 rpm 400 to 600LMS

Viscosity, EN 12092 - MV, 25 °C, after 180 s, mPa·s (cP):

Shear rate 129 s-1 300 to 600

3:Typical Properties of cured material 

Physical Properties

Coefficient of Thermal Expansion, ASTM D 696, K-1 80×10-6

Coefficient of Thermal Conductivity, ASTM C177,

W/(m·K)

0.1

Specific Heat, kJ/(kg·K) 0.3

4:Typical Performance of cured material 

Adhesive Properties

Cured for 15 minutes @ 22 °C

Compressive Shear Strength, ISO 10123:

Steel pins and collars N/mm² ≥13.5LMS

(psi) (≥1,957)

Cured for 24 hours @ 22 °C

Compressive Shear Strength, ISO 10123:

Steel pins and collars N/mm² ≥25LMS

(psi) (≥3,625)

5:For Assembly

(1). For best results, clean all surfaces(external and internal) with a HYBOND cleaning solvent and allow to dry.

(2). If the material is an inactive metal or the cure speed is too slow, spray with Activator  7649™ and allow to dry.

(3). For Slip Fitted Assemblies, apply adhesive around the leading edge of the pin and the inside of the collar and use a rotating motion during assembly to ensure good coverage.

(4). For Press Fitted Assemblies, apply adhesive thoroughly to both bond surfaces and assemble at high press on rates.

(5). For Shrink Fitted Assemblies the adhesive should be coated onto the pin, the collar should then be heated to create sufficient clearance for free assembly.

(6). Parts should not be disturbed until sufficient handling strength is achieved

6:For Disassembly

Apply localized heat to the assembly to approximately 250 °C. Disassemble while hot.

7:For Clean up

Cured product can be removed with a combination of soaking in a HENG YING solvent and mechanical abrasion such as a wire brush.

8:Storage

Store product in the unopened container in a dry location. Storage information may be indicated on the product container labeling.

Optimal Storage: 8 °C to 21 °C. Storage below 8 °C or greater than 28 °C can adversely affect product properties. Material removed from containers may be contaminated during use. Do not return product to the original container.HYBOND Corporation cannot assume responsibility for product which

has been contaminated or stored under conditions other than those previously indicated. If additional information is required, please contact us.

� �"f n I� �Ƈ 宋体; font-size:10.5000pt; mso-font-kerning:0.0000pt; " >

7. Cure Speed vs. Activator

Where cure speed is unacceptably long due to large gaps, applying activator to the surface will improve cure speed. However, it can reduce ultimate strength of the bond effect.

8. Directions for use:

(1). Bond areas should be clean and free from grease. Clean all surfaces with a HYBOND cleaning solvent and allow to be dried.

(2). HYBOND Primer may be applied to the bond area. Avoid applying excess Primer. Allow the Primer to dry.

(3). HYBOND Activator may be used if necessary. Apply HYBOND Activator to one bond surface (do not apply activator to the primed surface where Primer is also used). Allow the Activator to dry 

(4). Apply adhesive to one of the bond surfaces (do not apply the adhesive to the activated surface). Do not use items like tissue or a brush to spread the adhesive. Assemble the parts within a few seconds. The parts should be accurately located, as the short fixture time leaves little opportunity for adjustment.

(5). HYBOND Activator can be used to cure fillets of product outside the bond area. Spray or drop the activator on the excess product.

(6). Bonds should be held fixed or clamped until adhesive has fixtured.

(7). Product should be allowed to develop full strength before subjecting to any service loads (typically 24 to 72 hours after assembly, depending on bond gap, materials and ambient conditions).

9.Storage

Store product in the unopened container in a dry location, storage instruction is shown on the label of bottle

Optimal Storage: 2 °C to 8 °C. Storage below 2 °C or greater than 8 °C can adversely affect product properties. Material removed from containers may be contaminated during use. Do not return product to the original container. Heng ying Corporation cannot assume responsibility for product which has been contaminated or stored under conditions other than those previously indicated. If additional information is required, please contact us.

Loctite 641 Quality Medium strength Bearing Fit

                     Loctite 641 Quality Medium strength Bearing Fit 

Product Description
CNHYBOND 641™ provides the following product

characteristics:
Technology: Acrylic

Chemical Type:methacrylate Ester

Appearance(uncured):yellow liquid

Components:One component - requires no mixing

Viscosity:Medium

Cure:Anaerobic

Secondary Cure:Activator

Application:Retaining

Strength:Medium

CNHYBOND 641™ is designed for the bonding of cylindrical fitting parts. particularly where disassembly is required for service operations. The product cures when confined in the absence of air between close fitting metal surfaces and prevents loosening and leakage from shock and vibration. Typical applications include retention of bearings onto shafts and into housings.

Typical Properties of Uncured Material 

Specific Gravity @ 25 °C 1.0

Flash Point - See MSDS

Viscosity, Brookfield - RVT, 25 °C, mPa·s (cP):

Spindle 2, speed 20 rpm ,200 to 2,600LMS

Viscosity, EN 12092 - MV, 25 °C, after 180 s, mPa·s (cP):

Shear rate 129 s-1 90-180

3:Typical Properties of Cured Material 

Physical Properties

Coefficient of Thermal Expansion,ASTM D696,K-1 80×10-6

Coefficient of Thermal Conductivity, ASTM C177,W/(m·K)  0.1
Specific Heat, kJ/(kg·K) 0.3

4:Typical Performance of Cured Material 

Adhesive Properties

Adhesive Properties  Cured for 15 minutes @ 22 °C
Compressive Shear Strength, ISO 10123:

Steel pins and collars N/mm² ≥6.5LMS   (psi) (≥940)

5:For Assembly

(1). For best results, clean all surfaces (external and internal) with a HYBOND  cleaning solvent and allow to dry.

(2). If the material is an inactive metal or the cure speed is too slow, spray with Activator  7649™ and allow to dry.

(3). For Slip Fitted Assemblies, apply adhesive around the leading edge of the pin and the inside of the collar and use a rotating motion during assembly to ensure good coverage.

(4). For Press Fitted Assemblies, apply adhesive thoroughly to both bond surfaces and assemble at high press on rates.

(5). For Shrink Fitted Assemblies the adhesive should be coated onto the pin, the collar should then be heated to create sufficient clearance for free assembly.

(6). Parts should not be disturbed until sufficient handling strength is achieved

6:For Disassembly

Apply localized heat to the assembly to approximately 250 °C. Disassemble while hot.

7:For Clean up

Cured product can be removed with a combination of soaking in a HENG YING solvent and mechanical abrasion such as a wire brush.

8:Storage

Store product in the unopened container in a dry location. Storage information may be indicated on the product container labeling.

Optimal Storage: 8 °C to 21 °C. Storage below 8 °C or greater than 28 °C can adversely affect product properties. Material removed from containers may be contaminated during use. Do not return product to the original container.HYBOND Corporation cannot assume responsibility for product which has been contaminated or stored under conditions other than those previously indicated. If additional information is required, please contact us.

Loctite 638 Quality High Strength Fast Cure Retainer

           Loctite 638 Quality High Strength Fast Cure Retainer

                                                                   from Tina(hengying@cnhybond.com  0086-18927302778  Skype:hengying11)

1:Product Description 

HYBOND 638 provides the following product characteristics:

Technology: Acrylic

Chemical Type: Urethane methacrylate

Appearance (uncured): Green  liquidLMS

MComponents:  One component - requires no mixing

Viscosity: high

Cure : Anaerobic

Secondary Cure: Activator

Application:Retaining

Strength: high

HYBOND 638™ is designed for the bonding of cylindrical fitting parts, particularly where bond gaps can approach 0.25 mm and where maximum strength at room temperature is required. The product cures when confined in the absence of air between close fitting metal surfaces and prevents loosening and leakage from shock and vibration. Typical applications include locking bushings and sleeves into housings and on shafts.

2: Typical Properties of Uncured Material 

Specific Gravity @ 25 °C 1.09

Flash Point - See MSDS

Viscosity, Brookfield - RVT, 25 °C, mPa·s (cP):

Spindle 3, speed 20 rpm 2,000 to 3,000LMS

Viscosity, EN 12092 - MV, 25 °C, after 180 s, mPa·s (cP):

Shear rate 129 s-1 1,500 to 3,000

3:Typical Properties of Cured Material 

Physical Properties

Coefficient of Thermal Expansion,ISO 11359-2, K-1   80×10-6

Coefficient of Thermal Conductivity,W/(m·K)  0.1

Specific Heat, kJ/(kg·K) 0.3

4:Typical Performance of Cured Material 

Adhesive Properties

After 24 hours @ 22 °C

Compressive Shear Strength, ISO 10123:

Steel pins and collars N/mm² ≥25LMS   (psi) (3,625)

After 15 minutes @ 22 °C

Compressive Shear Strength, ISO 10123:

Steel pins and collars N/mm² ≥13.5LMS   (psi) (1,960

5:For Assembly

(1). For best results, clean all surfaces (external and internal) with a HYBOND  cleaning solvent and allow to dry.

(2). If the material is an inactive metal or the cure speed is too slow, spray with Activator  7649™ and allow to dry.

(3). For Slip Fitted Assemblies, apply adhesive around the leading edge of the pin and the inside of the collar and use a rotating motion during assembly to ensure good coverage.

(4). For Press Fitted Assemblies, apply adhesive thoroughly to both bond surfaces and assemble at high press on rates.

(5). For Shrink Fitted Assemblies the adhesive should be coated onto the pin, the collar should then be heated to create sufficient clearance for free assembly.

(6). Parts should not be disturbed until sufficient handling strength is achieved

6:For Disassembly

Apply localized heat to the assembly to approximately 250 °C. Disassemble while hot.

7:For Clean up

Cured product can be removed with a combination of soaking in a HENG YING solvent and mechanical abrasion such as a wire brush.

8:Storage

Store product in the unopened container in a dry location. Storage information may be indicated on the product container labeling.

Optimal Storage: 8 °C to 21 °C. Storage below 8 °C or greater than 28 °C can adversely affect product properties. Material removed from containers may be contaminated during use. Do not return product to the original container.HYBOND Corporation cannot assume responsibility for product which has been contaminated or stored under conditions other than those previously indicated. If additional information is required, please contact us.

Loctite 620 Quality High Temperature Cylindrical bonding Retaining Compound

Loctite 620 Quality High Temperature Cylindrical bonding Retaining Compound

                                                                                    from Tina(hengying@cnhybond.com  0086-18927302778  Skype:hengying11)

1:Product Description 

HYBOND 620 provides the following product characteristics:

Technology: Acrylic

Chemical Type: methacrylate ester

Appearance (uncured): Green  liquidLMS

MComponents: One component - requires no mixing

Viscosity: high

Cure : Anaerobic

Secondary Cure: Activator

Application :Retaining

Strength: Medium to high

HYBOND 620 is designed for the bonding of cylindrical fitting parts. The product cures when confined in the absence of air between close fitting metal surfaces and prevents loosening and leakage from shock and vibration. Typical applications include locating pins in radiator assemblies, sleeves into pump housings and bearings in auto transmissions. Particularlysuitable for applications where temperature resistance up to 200°C is required.

2: Typical Properties of Uncured Material 

M LM Specific Gravity @ 25 °C 1.16

Flash Point - See MSDS

Viscosity, Brookfield - RVT, 25 °C, mPa·s (cP):

Spindle 5, speed 20 rpm 5,000 to 12,000LMS

Viscosity, EN 12092 - MV, 25 °C, after 180 s, mPa·s (cP):

Shear rate 129 s-1 1,200 to 2,400S

3:Typical Properties of Cured Material 

Physical Properties:

Coefficient of Thermal Expansion, ASTM D 696, K-1 80×10-6

Coefficient of Thermal Conductivity, ASTM C 177, W/(m·K) 0.10

Specific Heat, kJ/(kg·K) 0.30

Elongation, at break, ASTM D 412, % <1

4:Typical Performance of Cured Material 

Adhesive Properties

After 24 hours @ 22 °C

Compressive Shear Strength, ISO 10123:

Steel pins and collars N/mm² ≥17.20LMS

(psi) (2,495)

Cured for 24 hours @ 22 °C, followed by 24 hours @ 177 °C,

tested @ 22 °C

Compressive Shear Strength, ISO 10123:

Steel pins and collars N/mm² ≥24.10LMS

(psi) (3,495)

5:For Assembly

(1). For best results, clean all surfaces (external and internal) with a HYBOND cleaning solvent and allow to dry.

(2). If the material is an inactive metal or the cure speed is too slow, spray with Activator  7649™ and allow to dry.

(3). For Slip Fitted Assemblies, apply adhesive around the leading edge of the pin and the inside of the collar and use a rotating motion during assembly to ensure good coverage.

(4). For Press Fitted Assemblies, apply adhesive thoroughly to both bond surfaces and assemble at high press onrates.

(5). For Shrink Fitted Assemblies the adhesive should be coated onto the pin, the collar should then be heated to create sufficient clearance for free assembly.

6:For Disassembly

Apply localized heat to the assembly to approximately 250 °C. Disassemble while hot.

7:For Clean up

Cured product can be removed with a combination of soaking in a HENG YING solvent and mechanical abrasion such as a wire brush.

8:Storage

Store product in the unopened container in a dry location. Storage information may be indicated on the product container labeling.

Optimal Storage: 8 °C to 21 °C. Storage below 8 °C or greater than 28 °C can adversely affect product properties. Material removed from containers may be contaminated during use. Do not return product to the original container.HYBOND Corporation cannot assume responsibility for product which has been contaminated or stored under conditions other than those previously indicated. If additional information is required, please contact us.

Loctite 609 Equivalent Bearing Mount (Green) Retaining Compound

        Loctite 609 Equivalent Bearing Mount (Green) Retaining Compound

                                                                from Tina(hengying@cnhybond.com   0086-18927302778  Skype:hengying11)

1:PRODUCT DESCRIPTION

HYBOND 609 provides the following product characteristics:

Technology: Acrylic

Chemical Type: methacrylate ester

Appearance (uncured): Green  liquidLMS

MSComponents: One component - requires no mixing

Viscosity: low

Cure : Anaerobic

Secondary Cure: Activator

Application :Retaining

Strength: Medium

HYBOND609 is designed for the bonding of cylindrical fitting parts. The product cures when confined in the absence of air between close fitting metal surfaces and prevents loosening and leakage from shock and vibration. Typical applications include rotor to shafts in fractional and subfractional horsepower motors. Locks bushings and sleeves in housings on shafts. Augments press fits.

Mil-R-46082B

HYBOND 609 is tested to the lot requirements of Military

Specification Mil-R-46082B.

2: TYPICAL PROPERTIES OF UNCURED MATERIAL

M Specific Gravity @ 25 °C 1.10

Flash Point - See MSDS

Viscosity, Cannon Fenske #300, ISO 3104, mPa·s (cP) 110 to 140LMS

3:TYPICAL PROPERTIES OF CURED MATERIAL

Physical Properties:

Coefficient of Thermal Expansion, ASTM D 696, K-1 80×10-6

Coefficient of Thermal Conductivity, ASTM C 177,

W/(m·K)

0.10

Specific Heat, kJ/(kg·K) 0.30

Elongation, at break, ASTM D 412, % <2

4::TYPICAL PERFORMANCE OF CURED MATERIAL

Adhesive Properties

After 24 hours @ 22 °C

Compressive Shear Strength, ISO 10123:

Steel pins and collars N/mm² ≥15.80LMS

(psi) (≥2,290)

After 1 hour @ 22 °C

Compressive Shear Strength, ISO 10123:

Steel pins and collars N/mm² ≥10.30LMS

(psi) (≥1,490)5

5:For Assembly

(1). For best results, clean all surfaces (external and internal) with a HYBOND  cleaning solvent and allow to dry.

(2). If the material is an inactive metal or the cure speed is too slow, spray with Activator  7649™ and allow to dry.

(3). For Slip Fitted Assemblies, apply adhesive around the leading edge of the pin and the inside of the collar and use a rotating motion during assembly to ensure good coverage.

(4). For Press Fitted Assemblies, apply adhesive thoroughly to both bond surfaces and assemble at high press onrates.

(5). For Shrink Fitted Assemblies the adhesive should be coated onto the pin, the collar should then be heated to create sufficient clearance for free assembly.

(6). Parts should not be disturbed until sufficient handling strength is achieved.

6:For Disassembly

Apply localized heat to the assembly to approximately

250 °C. Disassemble while hot.

7:For Clean up

Cured product can be removed with a combination of soaking in a HENG YING solvent and mechanical abrasion such as a wire brush.

8:Storage

Store product in the unopened container in a dry location. Storage information may be indicated on the product container labeling.

Optimal Storage: 8 °C to 21 °C. Storage below 8 °C or greater than 28 °C can adversely affect product properties. Material removed from containers may be contaminated during use. Do not return product to the original container.HYBOND Corporation cannot assume responsibility for product which

has been contaminated or stored under conditions other than those previously indicated. If additional information is required, please contact us.

Loctite 603 Equivalent General Purpose Retaining Compound

                  Loctite 603 Equivalent General Purpose Retaining Compound

                                                        from Tina(hengying@cnhybond.com      0086-18927302778  Skype:hengying11)

1:PRODUCT DESCRIPTION

HYBOND 603 provides the following product characteristics:

Technology: Acrylic

Chemical Type: Urethane methacrylate

Appearance (uncured): Green  liquidLM

MSComponents: One component - requires no mixing

Viscosity: low

Cure : Anaerobic

Secondary Cure: Activator

Application :Threadlocking

Strength: High

HYBOND  603 is designed for the bonding of cylindrical fitting parts, particularly where consistently surfaces cannot be assured. The product cures when confined in the absence of air between close fitting metal surfaces and prevents loosening and leakage from shock and vibration. Typical applications include retaining roller bearings or oil impregnated bushings into housings.

2: TYPICAL PROPERTIES OF UNCURED MATERIAL

MSSpecific Gravity @ 25 °C 1.1

Flash Point - See MSDS

Viscosity, Brookfield - RVT, 25 °C, mPa·s (cP):

Spindle 1, speed 20 rpm 100 to 150LMS

Viscosity, EN 12092 - MV, 25 °C, after 180 s, mPa·s (cP):

Shear rate 277 s-1 90 to 180

3:TYPICAL PERFORMANCE OF CURED MATERIAL

Adhesive Properties

After 24 hours @ 22 °C

Compressive Shear Strength, ISO 10123:

Steel pins and collars N/mm² ≥22.5LMS

(psi) (3,260)

After 30 minutes @ 22 °C

Compressive Shear Strength, ISO 10123:

Steel pins and collars N/mm² ≥13.5LMS

(psi) (1,960)

4:For Assembly

1. For best results, clean all surfaces (external and internal) with a HYBOND  cleaning solvent and allow to dry.

2. If the material is an inactive metal or the cure speed is too slow, spray with Activator  7649™ and allow to dry.

3. For Slip Fitted Assemblies, apply adhesive around the leading edge of the pin and the inside of the collar and use a rotating motion during assembly to ensure good coverage.

4. For Press Fitted Assemblies, apply adhesive thoroughly to both bond surfaces and assemble at high press on rates.

5. For Shrink Fitted Assemblies the adhesive should be coated onto the pin, the collar should then be heated to create sufficient clearance for free assembly.

6. Parts should not be disturbed until sufficient handling

strength is achieved.

For Porosity Sealing

1. Clean area and apply localized heat to the area to

approximately 121°C.

2. Allow to cool to approximately 85°C and apply the

product.

5:For Disassembly

Apply localized heat to the assembly to approximately

250 °C. Disassemble while hot.

6:For Clean up

Cured product can be removed with a combination of soaking in a HENG YING solvent and mechanical abrasion such as a wire brush.

7:Storage

Store product in the unopened container in a dry location. Storage information may be indicated on the product container labeling.

Optimal Storage: 8 °C to 21 °C. Storage below 8 °C or greater than 28 °C can adversely affect product properties. Material removed from containers may be contaminated during use. Do not return product to the original container.HYBOND Corporation cannot assume responsibility for product which has been contaminated or stored under conditions other than those previously indicated. If additional information is required, please contact us.